Tangit FP100 Fire Protection 1C Foam
Single component acrylic sealant for fire resistant and smoke tight closing of linear building joints in walls and ceilings acc. EN 1366-4
PROPERTIES
- Fire resistant and smoke tight from EI60 up to EI240
- Tested according EN 1366-4
- Fire resistant class B acc. EN13501 and B1 acc.DIN4102
- High yield of approx. 45 litres per can
- Quick curing: teck-free after 5-8 minutes, can be cut after approx. 7-10 minutes
- Additional thermal and acoustic protection
- Simple, fast and clean handling
- Free of propellant
TESTING AND APPROVAL
Tested and certified according EN 1366-4
APPLICATION SCOPE
For fire-resistant and smoke-tight closing of linear joints ≤45mm in walls and ceilings according EN 1366-4.
| TECHNICAL INFORMATION | |
| Material: | 1c polyurethane |
| Color: | light green |
| Yield (750 ml): | up to 45 litres |
| Bulk density: | approx. 15 kg/m3 |
| Cell-structure: | medium |
| Tack-free: | 5-8 minutes |
| Can be cut after (20 mm bead): | 7-10 minutes |
| Stability load bearing (20 mm bead): | after approx. 12 hours |
| Minimum working temperature (Can, application surfaces): | + 5oC |
| Maximum working temperature (Can, application surfaces) : | +30oC |
| Optimum working temperature (Can, application surfaces): | +20oC |
| Tensile strength (DIN 53430): | 8-10 N/cm2 |
| Elongation at tension (DIN 53430): | approx. 18 % |
| Shear strength (DIN 53427): | 4-5 N/cm2 |
| Compressive strength at 10% stress (DIN 53421): | 2-3 N/cm2 |
| Temperature resistance of the cured bead Long-term: | -40oC to + 80oC |